Quote:
Originally Posted by 87fleetsidedude
Is c25 best of straight Co2? It is only a 110v welder so i'm thinking i could get away with 100% with out too much trouble. but c25 would probably be better with the shallower penetration and minimized spatter. what do you think?
thanks, Justin
|
Stick with the mix. you don't need straight CO2 Either one will work but for thin gauge sheetmetal I would just use the mix. If you already have it, as it sounds it will work