I used solid mig .025 steel wire. Not the best choice I know but those were my circumstances. What should be used is stainless wire 308, and should be using trimix gas much better looking weld ( helium, co, argon).
Edit:. And you should really weld a continuous bead rather than spot welding like I did. I'm still figuring this crap out... However I didn't allow any cool down time between spot welds, and I did circular patterns to make sure they overlapped the previous weld so they are joined together decent.
|